In this work, Al-7Si-0.3Mg alloy was studied. The alloy conditions was selected to be as-received, AlB3 grain refined and Sr modified. For each parameter, castings were made before and after degassing. In order to quantify the melt quality, reduced pressure test was used and bifilm index measurements were made. All the cast parts were subjected to metallographical examination, and thus, porosity measurements, distribution, area fraction were compared for each of the casting conditions.
Eser Adı (dc.title) | Grain Refinement, Modification, Degassing and Melt Quality Relationship in Al-7Si-0.3Mg |
Yayın Türü (dc.type) | Makale |
Yazar/lar (dc.contributor.author) | ÇETİN, Remzi |
Yazar/lar (dc.contributor.author) | ULUDAĞ, Muhammet |
Yazar/lar (dc.contributor.author) | DIŞPINAR, Derya |
Atıf Dizini (dc.source.database) | Diğer |
Konu Başlıkları (dc.subject) | Casting |
Konu Başlıkları (dc.subject) | Porosity |
Konu Başlıkları (dc.subject) | Casting Quality |
Konu Başlıkları (dc.subject) | Modification |
Konu Başlıkları (dc.subject) | Grain Refinement |
Yayın Tarihi (dc.date.issued) | 2014 |
Kayıt Giriş Tarihi (dc.date.accessioned) | 2019-07-09T14:26:26Z |
Açık Erişim tarihi (dc.date.available) | 2019-07-09T14:26:26Z |
ISSN (dc.identifier.issn) | 1541-1548 |
ISSN (dc.identifier.issn) | 1541-1548 |
Özet (dc.description.abstract) | In this work, Al-7Si-0.3Mg alloy was studied. The alloy conditions was selected to be as-received, AlB3 grain refined and Sr modified. For each parameter, castings were made before and after degassing. In order to quantify the melt quality, reduced pressure test was used and bifilm index measurements were made. All the cast parts were subjected to metallographical examination, and thus, porosity measurements, distribution, area fraction were compared for each of the casting conditions. |