Detaylı Arama
İptal
Bulunan: 2 Adet 0.000 sn
- Eklemek veya çıkarmak istediğiniz kriterleriniz için 'Dahil' / 'Hariç' seçeneğini kullanabilirsiniz. Sorgu satırları birbirine 'VE' bağlacı ile bağlıdır.
- İptal tuşuna basarak normal aramaya dönebilirsiniz.
Filtreler
Filtreler
Bulunan: 2 Adet 0.000 sn
Yayın Tarihi : 2017 ✕Konu Başlıkları : A356 Alloy ✕
Koleksiyon [3]
Ambargo Durumu [1]
Tam Metin [1]
Yayın Türü [1]
Yazar/lar [6]
Atıf Dizini [2]
Konu Başlıkları [7]
Yayıncı [2]
Yayın Tarihi [1]
Yayın Dili [1]
Erişime Açık

Effect of Sr and Ti Addition on the Corrosion Behavior of Al-7Si-0.3Mg Alloy

ÇETİN, Remzi | ULUDAĞ, Muhammet | KOÇABAŞ, Mustafa | DIŞPINAR, Derya | CANSEVER, Nurhan

In the present study, the corrosion behaviour of A356 (Al-7Si-0.3Mg) alloy in 3.5% NaCl solution has been evaluated using cyclic/potentiodynamic polarization tests. The alloy was provided in the unmodified form and it was then modified with AlTi5B1 for grain refinement and with AlSr15 for Si modifications. These modifications yield to better mechanical properties. Tensile tests were performed. In addition, bifilm index and SDAS values were calculated and microstructure of the samples was investigated. As a result of the corrosion test, the Ecorr values for all conditions were determined approx ...Daha fazlası

Makale 2017 Archives of Foundry Engineering 3 Görüntülenme
Erişime Açık

Characterization of the Effect of Melt Treatments on Melt Quality in Al-7wt %Si-Mg Alloys

ÇETİN, Remzi | ULUDAĞ, Muhammet | DIŞPINAR, Derya | TİRYAKİOĞLU, Murat

The effects of degassing, holding time and melt additions (Sr, Sr + Ti, Ti, B and B + Sr) on the quality of A356 melts were examined. A total of 120 reduced pressure test samples were collected. Pores in these samples were analyzed via digital image processing to determine the number density of pores as well as the statistical distribution of their sizes. Results showed that in all cases, degassing with argon reduced the number of defects regardless of the additions made to the melts. Moreover, all additions were found to degrade melt quality. The lowest number density of pores in all melts wa ...Daha fazlası

Makale 2017 METALS 6 Görüntülenme
6698 sayılı Kişisel Verilerin Korunması Kanunu kapsamında yükümlülüklerimiz ve cerez politikamız hakkında bilgi sahibi olmak için alttaki bağlantıyı kullanabilirsiniz.
Tamam Açık Erişim PolitikasıAçık Erişim Yönergesi
creativecommons
Bu site altında yer alan tüm kaynaklar Creative Commons Alıntı-GayriTicari-Türetilemez 4.0 Uluslararası Lisansı ile lisanslanmıştır.
Platforms